Silicon carbide/alumina/zirconia porous ceramic foam filter for cast iron

Ceramic foam filter is just developed as a new type of molten metal filters to decrease casting flaw in recent years. It is made from high quality ceramic materials, whose main&nbs

Featured Products

Ceramic foam filter is just developed as a new type of molten metal filters to decrease casting 
flaw in recent years. It is made from high quality ceramic materials, whose main components 
are Al2O3, SiC, ZrO2, MgO etc. Ceramic Foam Filter has the characters of light weight, high 
mechanical strength, large specific surface areas, high porosity, excellent thermal shock resistance, 
chemical corrosion resistance and high temperature stability in molten metal. With the distributing 
pores net structure, they are able to increase the surface areas, and absorb the sinter, the liquid metal 
becomes more pure, waster quality problems such as sand pore and air pore are much less and 
the cast quality becomes much better.

We can supply ceramic foam filters are as follows:
1. Silicon Carbide Ceramic Foam Filter is applied to purge and filter solution of ductile iron 
casting, grey iron and other iron casting.

2. Zirconia Ceramic Foam Filter is applied to purge and filter solution of steel high temperature 
metal such as steel alloy stainless steel etc.

3. Magnesia Ceramic Foam Filter is applied to purge and filter solution of magnesium and 
magnesium alloy.

4. Alumina Ceramic Foam Filter is applied to purge and filter solution of aluminium and 
aluminium alloys.

Specifications Ceramic Foam Filter for foundry iron/steel/alumina casting 
1.Material: Al2O3, SiC, ZrO2, MgO 
2.Bore density: 10-60 PPI
Sic/Alumina/Zirconia Porous Ceramic Foam Filters for Iron Casting
TypeAlumina CFFSilicon carbide CFFZirconia CFFMagnesia CFF
Applied temperature≤1200 º C≤1500 º C≤1700 º C≤1100 º C
ColorWhiteGrey blackYellowYellow
Bulk Density0.35~0.55g/cm30.45~0.65g/cm31~1.5g/cm30.5~0.7g/cm3
Bore Density10~60PPI10~60PPI10~60PPI10-60ppi
Bending Strength0.6Mpa0.8Mpa0.8-1.0Mpa0.6Mpa
Compression Strength≥0.8Mpa≥1.0Mpa≥1.5Mpa≥0.8Mpa
Thermal Shock ResistanceNot break after 6 times thermal shock testing
(1100 º C ~ Room Temperature)
ApplicationMolten Aluminum and AlloyMolten Iron and AlloyMolten Stainless Steel, Alloy and other metal in precision moldingMolten magnesium and its alloys

Contact us